Polymaker Polylite PLA Galaxy Dark Grey 1.75mm (1kg)

Property

Testing Method

Typical Value

Density

ISO1183, GB/T1033

1.17 g/cm³ at 23°C

Melt index

210°C, 2.16kg

7-11 g/10min

Property

Testing Method

Typical Value

Young’s modulus (X-Y)

ISO 527, GB/T 1040

3426.9 ± 64.8 MPa

Young’s modulus (Z)

3064.9 ± 83.4 MPa

Tensile strength (X-Y)

ISO 527, GB/T 1040

52.3 ± 0.3 MPa

Tensile strength (Z)

40.5 ± 0.5 MPa

Elongation at break (X-Y)

ISO 527, GB/T 1040

6.3 ± 0.6 %

Elongation at break (Z)

1.8 ± 0.1 MPa

Bending modulus (X-Y)

ISO 178, GB/T 9341

3230.9 ± 55.3 MPa

Bending modulus (Z)

N/A

Bending strength (X-Y)

ISO 178, GB/T 9341

86.9 ± 1.2 MPa

Bending strength (Z)

N/A

Charpy impact strength (X-Y)

ISO 179,  GB/T 1043

3.3 ±0.2 kJ/m²

Charpy impact strength (Z)

N/A

Parameter

Nozzle temperature

190 – 230 (℃)