PolyLite™ PLA is a high-quality PLA
designed for reliability and ease of printing.
Property |
Testing Method |
Typical Value |
Density |
ISO1183,
GB/T1033 |
1.17
g/cm3 at 23°C |
Melt index |
210°C, 2.16kg |
7-11 g/10min |
Property |
Testing Method |
Typical Value |
Young’s
modulus (X-Y) |
ISO 527,
GB/T 1040 |
3426.9
± 64.8 MPa |
Young’s modulus (Z) |
3064.9 ± 83.4 MPa |
|
Tensile
strength (X-Y) |
ISO 527,
GB/T 1040 |
52.3
± 0.3 MPa |
Tensile strength (Z) |
40.5 ± 0.5 MPa |
|
Elongation
at break (X-Y) |
ISO 527,
GB/T 1040 |
6.3
± 0.6 % |
Elongation at break (Z) |
1.8 ± 0.1 MPa |
|
Bending
modulus (X-Y) |
ISO
178, GB/T 9341 |
3230.9
± 55.3 MPa |
Bending modulus (Z) |
N/A |
|
Bending
strength (X-Y) |
ISO
178, GB/T 9341 |
86.9
± 1.2 MPa |
Bending strength (Z) |
N/A |
|
Charpy
impact strength (X-Y) |
ISO 179, GB/T 1043 |
3.3
±0.2 kJ/m2 |
Charpy impact strength (Z) |
N/A |
*
Based on 0.4 mm nozzle Printing conditions may vary with different
nozzle diameters
Parameter |
|
Nozzle
temperature |
190 – 230 (℃) |
Build surface material |
|