PolyTerra™ PLA+ filament contains organic material
than ordinary PLA which brings better layer adhesion and extra toughness.
* Based on 0.4 mm nozzle and Simplify 3D v.4.0.
Printing conditions may vary with different nozzle diameters
RECOMMENDED PRINTING PARAMETERS
Parameter |
Typical value |
Nozzle temperature |
190 – 220 (℃) |
Build surface material |
BuildTak® , Glass, Blue Tape |
Build surface treatment |
Glue, Magigoo |
Build plate temperature |
30 - 60 (˚C) |
Cooling fan |
ON |
Printing speed |
30 - 70 (mm/s) |
Raft separation distance |
0.2 (mm) |
Retraction distance |
1 - 3 (mm) |
Retraction speed |
30 - 60 (mm/s) |
Environmental temperature |
Room temperature – 45 (˚C) |
Threshold overhang angle |
60 (˚) |
Recommended support material |
Self-support |
|
Testing Method |
Typical Value |
Density |
ISO1183, GB/T1033 |
1.24 g/cm3 at 21.5°C |
Melt index |
210°C, 2.16kg |
8 g/10min |
MECHANICAL PROPERTIES
Property |
Testing Method |
Typical Value |
Young’s modulus (X-Y) |
ISO 527, GB/T 1040 |
2245.9 ± 90.7 MPa |
Young’s modulus (Z) |
1781.2 ± 53.2 MPa |
|
Tensile strength (X-Y) |
ISO 527, GB/T 1040 |
31.1 ± 0.8 MPa |
Tensile strength (Z) |
16.7 ± 0.4 MPa |
|
Elongation at break (X-Y) |
ISO 527, GB/T 1040 |
13.8 ± 2.9 % |
Elongation at break (Z) |
1.1 ± 0.1 MPa |
|
Bending modulus (X-Y) |
ISO 178, GB/T 9341 |
2441.9 ± 77.5 MPa |
Bending modulus (Z) |
N/A |
|
Bending strength (X-Y) |
ISO 178, GB/T 9341 |
58.7 ± 1.0 MPa |
Bending strength (Z) |
N/A |
|
Charpy impact strength (X-Y) |
ISO 179, GB/T 1043 |
5.9 ± 0.5 kJ/m2 |
Charpy impact strength (Z) |
N/A |