PolyLite™ PC is produced using a polycarbonate resin specifically engineered for 3D printing. It delivers good stiffness and heat resistance with light diffusing properties.
RECOMMENDED PRINTING CONDITIONS
Parameter | |
Nozzle temperature | 250 – 270 (℃) |
Build surface material | BuildTak® , Glass, PEI |
Build surface treatment | Magigoo |
Build plate temperature | 90 - 105 (˚C) |
Cooling fan | OFF |
Printing speed | 30-50 (mm/s) |
Raft separation distance | 0.2 (mm) |
Retraction distance | 1 (mm) |
Retraction speed | 20 (mm/s) |
Environmental temperature | 70-80 (˚C)(Recommended) |
Threshold overhang angle | 50 (˚) |
Recommended support material | PolyDissolve™ S2 |
PHYSICAL PROPERTIES
Property |
Testing Method |
Typical Value |
Density |
ISO1183,
GB/T1033 |
1.19
g/cm3 at 23°C |
Melt index |
260°C,
2.16kg |
8-11
g/10min |
Property |
Testing Method |
Typical Value |
Young’s modulus (X-Y) |
ISO 527, GB/T 1040 |
2497
± 154 MPa |
Young’s modulus (Z) |
2371
± 55 MPa |
|
Tensile strength (X-Y) |
ISO 527, GB/T 1040 |
69.1
± 3.0 MPa |
Tensile strength (Z) |
52.8
± 1.7 MPa |
|
Elongation at break (X-Y) |
ISO 527, GB/T 1040 |
4.8
± 0.9 % |
Elongation at break (Z) |
2.7
± 0.1 % |
|
Bending modulus (X-Y) |
ISO 178, GB/T 9341 |
2640
± 47 MPa |
Bending modulus (Z) |
N/A
|
|
Bending strength (X-Y) |
ISO 178, GB/T 9341 |
106.1
± 1.6 MPa |
Bending strength (Z) |
N/A
|
|
Charpy impact strength (X-Y) |
ISO 179,
GB/T 1043 |
4.1
± 0.9 kJ/m2 |
Charpy impact strength (Z) |
N/A
|
*
Specimens printed on Raise 3D E2 with 0.4mm
nozzle.